| SEPO 85 |
EPDM (Open Cell) |
Density : 0.08±0.03 g/cm³ |
Tensile Strength : 10 kg/cm² |
Elongation at Break : 200% |
Hardness (ESX60154): 50±5N |
Water Absorption : 0.08% |
Ozone Resistance : No cracking |
Compression Set : 29% |
Shrinkage : 0.1% |
Thickness : 3mm - 35mm |
Std. Size : 1m x 2m |
| SEP 140 |
EPDM |
Density : 0.14±0.03 g/cm³ |
Tensile Strength : 7.6 kg/cm² |
Elongation at Break : 200% |
Hardness (c type) : 15±3 HS |
Heat Shrinkage : 4% |
Compression Strength : 30±10 kg/100cm³ |
Compression Set : 25% |
Water Absorption : 0.005 g/cm³ |
Thickness : 1mm - 40mm |
Std. Size : 1m x 2m |
| SECON 100 |
EVA Conductive |
Density : 0.10 g/cm³ |
Tensile Strength : 12.1 kg/cm² |
Tear Strength : 4.5 kg/cm² |
Elongation at Break : 112% |
Hardness (c type) : 60 ~ 65 hs |
Water Absorption : 0.03 ≥ g/cm² |
Surface Resistance (Elec. Conductivity) : -105 Ω |
Thickness : 1mm - 25mm |
Std. Size : 1m x 1.5m |
| SEP 180 |
EPDM |
Density : 0.18±0.03 g/cm³ |
Tensile Strength : 8 kg/cm² |
Elongation at Break : 168% |
Hardness (c type) : 20±3 HS |
Heat Shrinkage : 4% |
Compression Strength : 35±10 kg/100cm³ |
Compression Set : 25% |
Water Absorption : 0.005 g/cm³ |
Thickness : 1mm - 40mm |
Std. Size : 1m x 2m |
| SHR 33 |
High Resilient Sponge |
Density : 0.033 g/cm³ |
Tensile Strength : 3 kgf/cm² |
Tear Strength : 1.5 kgf/cm² |
Elongation : 350% |
Heat Shrinkage : -3% |
Water Absorption : 0.003 g/cm² |
Hardness (c type) : HS 10 |
Thickness : 3mm - 40mm |
Std. Size : 1m x 2m |
| SCR 160 |
Neoprene / CR |
Density : 0.16±0.03 g/cm³ |
Tensile Strength : 4 kg/cm² |
Elongation at Break : 150% |
Hardness (c type) : 25±5 HS |
Heat Shrinkage : 4% |
Compression Strength : 30±10 kg/100cm² |
Compression Set : 25 kg/100cm² |
Water Absorption : 0.005 g/cm² |
Flammability : UL-94HF-1 pass |
Thickness : 1mm - 40mm |
Std. Size : 1m x 2m or Roll |
| SPE 65 |
Polyethylene Bun |
Density : ± 31 kg/m³ |
Tensile Strength : 304 kPa |
Tear Strength : 10 N/cm |
Elongation at Break : 153% |
Compression Strength : 34 kPa |
Hardness (00) : 65 ± 5 |
Water Absorption : 0.02% |
Thickness : 1mm - 75mm |
Std. Size : 1m x 2m or Roll |
| SCR 200 |
Neoprene / CR |
Density : 0.2±0.03 g/cm³ |
Tensile Strength : 8 kg/cm² |
Elongation at Break : 100% |
Hardness (c type) : 35±5 HS |
Heat Shrinkage : 3% |
Compression Strength : 80±10 kg/100cm² |
Compression Set : 25 kg/100cm² |
Water Absorption : 0.005 g/cm² |
Flammability : UL-94HF-1 pass |
Thickness : 1mm - 40mm |
Std. Size : 1m x 2m or Roll |
*Specific requirement of other grade of materials are also available upon request.
*Additional charges will incurred for other special thicknesses.
*Minimum Ordered Quantity is required for outstation and overseas order. |
|  |
| SPC 01 |
Natural Pure Cork |
Buoyancy : V.Good / Light Weight |
Specific Gravity : 0.25 |
Compressibility : 14,000ibs/cu.inch |
Resiliency : Excellent |
Impervious to water, oil, liquid |
Low density & thermal conductivity |
Ability to absorb vibration, stability, tough & durable |
Thickness : 1mm - 100mm |
Std. Size : 610mm x 910mm |
| SEV 035 |
EVA Foam |
Hardness : 35±3 (Type C) |
Tear Strength : 3.3 kgf/cm |
Tensile Strength : 8.5 kgf/cm² |
Elongation : 160% |
Density : 0.10±0.02 g/cm³ |
Resilience : 34% |
Shrinkage : 3% |
Hot Press Compression set : 93% |
Cold Press Compression set : 40% |
Thickness : 1mm - 45mm |
Std. Size : 1.2m x 2m |
| SRC 01 |
Rubberised Cork |
Tensile Strength : 35 kg/cm² |
Compression Set : 20% |
Recovery : 79% |
Oil Resistance : +5% |
Flexibility (F=5) : No Crack |
Fuel Resistance : +3% |
Thickness : 1mm - 20mm |
Std. Size : 900mm x 1800mm |
| SEV 055 |
EVA Foam |
Hardness : 55±3 (Type C) |
Tear Strength : 5 kgf/cm |
Tensile Strength : 14 kgf/cm² |
Elongation : 130% |
Density : 0.16±0.02 g/cm³ |
Resilience : 29% |
Shrinkage : 2% |
Hot Press Compression set : 80% |
Cold Press Compression set : 20% |
Thickness : 1mm - 38mm |
Std. Size : 1.2m x 2m |
| SRS 70 |
NBR Sponge |
Density : 60-80 kg/m³ |
Tensile Strength : 0.37 Mpa |
Tear Strength : 2445 N/m |
Elongation at Break : 80% |
Compression set at 50% deflection : 35% |
Water Absorption : 3% |
Oil Resistance change in mass : 360% |
Flame Retardant |
Thickness : 2mm - 50mm |
Std. Size : 914mmx 1219mm or Roll |
| SESD 25 |
ESD Foam |
Hardness : 20~30 (Type C) |
Density : 0.05~0.065 g/cm³ |
Tensile Strength : 4.5 kg/cm² |
Tear Strength : 2 kg/cm |
Elongation : 100% |
Compression Set : 15% |
Compression Deflection 25% : 0.35 kg/cm² |
Surface Resistivity : 1 x 106 ~ 9 x 108 Ω |
Volume Resisitivity :1 x 107 ~ 9 x 109 Ω |
Thickness : 2mm - 40mm |
Std. Size : 1m x 2m |
| SOS 70 |
NBR Open Cell |
Density : 0.07±0.01 g/cm³ |
Tensile Strength : 400 kPa |
Elongation : 90% + |
Tear Strength : 900 N/m + |
Load in 50% compression : 87±20 kPa |
Ability to Hold Water : 80mm + |
Flame Retardant |
Thickness : 3mm - 25mm |
Std. Size : 914mm x 1219mm |
| SESD 40 |
ESD Foam |
Hardness : 35~45 (Type C) |
Density : 0.05~0.065 g/cm³ |
Tensile Strength : 3.5 kg/cm² |
Tear Strength : 1 kg/cm |
Elongation : 40% |
Compression Set : 15% |
Compression Deflection 25% : 0.6 kg/cm² |
Surface Resistivity : 1 x 106 ~ 9 x 108 Ω |
Volume Resisitivity :1 x 107 ~ 9 x 109 Ω - cm |
Thickness : 2mm - 40mm |
Std. Size : 1m x 2m |
|
|
 |